Place of Origin: | China |
ब्रांड नाम: | UPCERA |
प्रमाणन: | CE、 FDA 、CFDA、KFDA |
Model Number: | ST-Color |
मूल्य: | Negotiation |
---|---|
Packaging Details: | Carton |
Payment Terms: | T/T |
Supply Ability: | 10 working days after received your payment |
Density before sintering (g/cm3): | 3.1±0.5 g/cm3 | Density after sintering (g/cm3): | 6.08±0.01 g/cm3 |
---|---|---|---|
CTE after sintering (25-200℃): | (10.5±1.0)x10-6K-1 | 3-point bending strength after sintering (MPa): | 1100Mpa |
Average transmittance: | 25~39% | Chemical solubility after sintering (μg/cm2): | < 100 |
Radioactivity after sintering (Bq/g): | <0.1 | Sintering temperature (℃): | 1450-1550℃Recommended 1530℃ |
हाई लाइट: | zirconium dioxide ceramic,dental ceramic materials |
Pre - shaded Machining Zirconium 98×12 mm Super Translucent with VITA 16 Colors
Specification
Wieland System |
Cerac in lab (Sirona)System |
Amann Girrbach System |
Zirkon zahn System CAD/CAM |
Upcera Open System |
D98*10 |
14*13*13 |
89*71*10 |
D95*10 |
D100*10 |
D98*12 |
20*14*15 |
89*71*12 |
D95*12 |
D100*12 |
D98*14 |
20*19*15 |
89*71*14 |
D95*14 |
D100*14 |
D98*16 |
40*14*15 |
89*71*16 |
D95*16 |
D100*16 |
D98*18 |
40*19*15 |
89*71*18 |
D95*18 |
D100*18 |
D98*20 |
55*19*15.5 |
89*71*20 |
D95*20 |
D100*20 |
D98*22 |
65*25*22 |
89*71*22 |
D95*22 |
D100*22 |
D98*25 |
65*40*22 |
89*71*25 |
D95*25 |
D100*25 |
|
85*40*22 |
|
|
|
FAQ
Q : Is the fit of crowns and bridges based on zirconia copings as good as that of PFM crowns and bridges?
A : Yes, the marginal fit of crowns and bridges fabricated from zirconia copings can be as good or better than PFM crowns and bridges.
Q : Is the fit of a zirconia coping important since the zirconia ceramic is so strong?
A: The thicker the cement the weaker the all-ceramic restoration. Cements are not as rigid as zirconia ceramic, so a thicker cement layer will cause more flexural deformation of a ceramic core, increasing the potential for fracture.
Q : Is it ok to grind on a zirconia coping without water spray?
A: Water spray is necessary when grinding on a zirconia ceramic coping. The white light or hot spot you see between a diamond and a zirconia ceramic has been measured at 1500 ºC. If the temperature of zirconia ceramic rises above 1000 ºC, a phase change can occur that will induce cracking and surface defects, lowering the strength of the coping.
व्यक्ति से संपर्क करें: sales
दूरभाष: +8613438862501
बहुपरत चिकित्सकीय जिरक्रोनिया ब्लॉक सीई आईएसओ एफडीए प्रमाणित ज़िरकोआनी डेंटल सामग्री
चिकित्सकीय प्रयोगशाला मिलिंग आपूर्तिएं ज़िरकोनिया सीएडी सीएएम खाली टीटी व्हाइट 49% पारभासी
Cerec Zirconia Blocks Manul Milling System Compatible For Zirconium Dental Crowns
चीनी मिट्टी के बरतन के लिए सेरेक ज़िरकोनिया ब्लॉक 98 × 12 मिमी कम रेडियोधर्मी
ST व्हाइट ब्लैंक हाई ट्रांसलूसेंट जिरकोनिया डेंटल फॉर ओपन सिस्टम 16 शेड्स
एसटी व्हाईट डेंटल जिराकिया ब्लैंक 16 शेड्स अपकेरा सिस्टम संगत
डेंटल ज़िरकोनिया ब्लैंक एचटी ब्लॉक ओपन कैड / सीएएम सिस्टम के लिए उच्च पारभासी
Pre Sintered Dental Zirconia Blank St Multilayer For Sirona System
Super Transparent Dental Zirconia Blank 16 Colors Without Coloring Liqiuids